English 
Español- Modified PP
- High Gloss PP
- Flame Retardant PP
- Glass Fiber Reinforced PP
- Mineral Filled PP
- Flame Retardant & Halogen-free PP for Thin Sheet (0.4mm)
- Flame Retardant PP (halogen-free)
- Flame Retardant PP (Polypropylene)
- Modified PA6, PA66
- Glass Fiber Reinforced PA6
- High Flame Retardant PA66
- Flame Retardant PA66
- Flame Retardant Halogen-free PA66
- Glass Fiber Reinforced PA66
- Flame Retardant PA6 and PA66
- Zero Halogen Low Smoke & High Flame Retardant Cable Sheathing Compounds
- Modified PE
- Glass Fiber Reinforced PE
- Flame Retardant PE
- Flame Retardant PE
- Flame Retardant ABS
- Flame Retardant PC
- Rubber Antioxidant 4020 Masterbatch Pellets
- Modified PBT
- Glass Fiber 30 Reinforced & Flame Retardant PBT PBT-RG30
- Glass Fiber 20 Reinforced & Flame Retardant PBT PBT-RG20
- Flame Retardant Aluminum Hydrate
- Flame Retardant Magnesium Hydrate
- Plastic Granule for Auto Parts
- Flame Retardant Halogen Free
- Flame Retardant Fabric
- Modified Polypropylene
Flame Retardant PC
Our flame retardant PC is manufactured in accordance with the UL V-0 standard. It features high strength, outstanding over-all properties, good high temperature resistance, colorful appearance, as well as good high and low temperature impact resistance.
Application
(1) Plug and Socket
(2) Electrical Appliance Controller
(3) Shell of Electrical household Appliance
(4) Shell of Electric Meter
Parameters of Flame Retardant PC
| Test Project | Test Methods | Unit | Typical Values [1] |
| Tensile Stress | GB/T1040-92 | Mpa | ≥50 |
| Flexural Stress | GB/T9341-2000 | Mpa | ≥100 |
| Flexural Modulus | GB/T9341-2000 | Mpa | ≥1500 |
| Notched Impact Strength | GB/T1043-93 | KJ/m2 | ≥20 |
| Elongation At Break | GB/T1040-92 | % | ≥100 |
| Heat Distortion Temperature | GB/T1634-2004 | °C | 110-120 |
| MFR | GB/T3682-2000 | g/10min | 8-18 |
| Oxygen Index (Vertical Burning) | GB/T2408-1996 | 4mm | ≥28 |
| Testing Condition | 23±2°C, 50±5%RH | ||
[1] Typical Values are average statistics in lab for reference. They are not used as products standards.
[2] Properties of coloring materials may be different from the above statistics.
Processing Conditions
| Start Point | Range | ||
| Melt Temp. | 230°C | 220-240°C | |
| Barrel Zone Temp. | Rear | 215°C | 210-230°C |
| Center | 225°C | 200-230°C | |
| Front | 235°C | 220-240°C | |
| Mold Temp. | 70°C | 60-100°C | |
| Processing Temp. Limit | 260°C | ||
| Injection Speed | 60-90% | ||
| Back Pressure | 0-1.0MPa | ||
| Pre-Dry Requirements | 90-100°C, 3-6hr | ||
Note: All the statistics above are for reference and can be adjusted according to different requirements
In addition to flame retardant PC, we also provide modified PP, modified PBT, flame retardant pa66, etc. If you are in need of these fireproof products, please contact us directly! We are happy to serve you.
-
- Flame Retardant ABS Our flame retardant ABS is applicable to the shell of electrical equipment, electrical tool accessories, and circuit board base ...
-
- Flame Retardant PE The flame retardant PE granule has the following characteristics: excellent mechanical property, strong stress cracking resistance and chemical resistance. It is suitable for use in ...