Glass Fiber Reinforced,PA6,Fire Resistant Material,China Plastic Granule Manufacturer

Products

Home > Flame Retardant > Modified PA6, PA66 > Glass Fiber Reinforced PA6

Glass Fiber Reinforced PA6

Welcome to Lianlian! We are an ISO9001 and ISO14001 certified glass fiber reinforced PA6 manufacturer in China, and can provide a variety of fireproof products such as modified PP, flame retardant ABS, flame retardant magnesium hydrate, etc.

Glass Fiber Reinforced PA6 PA6-G30
Our glass fiber reinforced PA6 features good dimensional stability and less warpage, high strength, good high-temperature resistance, outstanding over-all properties and good appearance. This type of flame retardant is widely used for injection molding, auto accessories, machine parts, electrical tools and electronic appliance parts.

Properties of Glass Fiber Reinforced PA6

Test Project	Test Methods	Unit	Typical Values [1]
Tensile Stress	GB/T1040-92	Mpa	140-180
Flexural Stress	GB/T9341-2000	Mpa	200-280
Flexural Modulus	GB/T9341-2000	Mpa	6500-8500
Notched Impact Strength	GB/T1043-93	KJ/m²	≥15
Elongation At Break	GB/T1040-92	%	5-30
Heat Distortion Temperature	GB/T1634-2004	°C	≥215
MFR	GB/T3682-2000	g/10min	10-30
Testing Condition	23±2°C, 50±5%RH

[1] Typical Values are average statistics in lab for reference. They are not used as products standards.

Processing Conditions

		Start Point	Range
Melt Temp		270°C	265-285°C
Barrel Zone Temp.	Rear	245°C	220-250°C
	Center	265°C	255-280°C
	Front	270°C	260-285°C
Mold Temp.		60°C	50-70°C
Processing Temp. Limit		300°C
Injection Speed		Moderate to high
Pre-Dry Requirements		90~110°C, 4~6hr

Note: All the statistics above are for reference and can be adjusted according to different requirements.

In addition, we can also customize fire retardant according to customer's specific requirements. For inquiries, please contact us at any time! You can trust us as your security expert.