Plastic granule for auto parts is produced by adding special modifier, toughener, reinforcer and age resister into polypropylene resin. Finished granulous materials are often used in production of auto fender-guard, instrument panel, etc. Our auto part plastic granule is of excellent machining property, high mechanical property and good weather resistance.

Plastic Granule for Auto Parts
(Grade: QPZ-300-390)

Packaging Specification: Kraft bag with a plastic bag lining, 20/25 kg/bag.
Technical Parameters of Plastic Granule for Auto Parts

Test Items	Index Range	Test Standard
Melt Flow Rate (g/10min)	2-10	GB/T 3682-2000
Tensile Strength (MPa)	18-40	GB/T 1040-1992
Elongation at Break (%)	50-300	GB/T 1040-1992
Bending Strength (MPa)	30-60	GB/T 9341-2000
Bending Modulus (GPa)	1.5-3	GB/T 9341-2000
Notched Impact Strength (kJ/m2)	3-20	GB/T 1043-1993
Impact Strength (kJ/m2)	20-50	GB/T 1043-1993
Heat Deflection Temperature(oC)	80-130	GB 1633-2000
Ball Indentation Hardness (N/mm)	30-90	GB/T 3398-1982
Shrinkage Rate (%)	0.5-2	GB/T 15585-1995
Test Condition	Temperature: 23℃, Humidity: 50%

Lianlina is flame retardant material manufacturer, specializes in making PE, PBT, PP, ABS, PC fire resistant materials, auto part plastic granule and modified polypropylene. CREATE flame retardant plastic products are widely used in electronic appliance, auto parts, motorcycle parts, communication equipment and household appliance. Our company has passed ISO9001 quality and ISO14001 environmental management system certification. Customized plastic granules and product processing are also available in customer needs. We make our effort provide safe and quality flame retardant materials at wholesale price. Thanks!